Depends on the recipe, water content, your type of mold, etc.
Most recipes can be unmolded after 24 hours. Salt/brine bars can be unmolded in a few hours. High soft oil/water recipes might take 3 days before they're hard enough!
I like to pull back the corner of my silicon mold and gently press on the corner of the loaf. If it easily dents in, it's not ready. If it holds its shape well like aged cheddar, it's good to go. There's no hardfast rule! I prefer to wait a bit longer to ensure I don't dent my loaf with my fingers.
Most recipes can be unmolded after 24 hours. Salt/brine bars can be unmolded in a few hours. High soft oil/water recipes might take 3 days before they're hard enough!
I like to pull back the corner of my silicon mold and gently press on the corner of the loaf. If it easily dents in, it's not ready. If it holds its shape well like aged cheddar, it's good to go. There's no hardfast rule! I prefer to wait a bit longer to ensure I don't dent my loaf with my fingers.
BroknArrw
Well-Known Member
I used candles and supplies goof proof recipe. 8 oz water, 6oz olive oil, 9.5oz Palm oil, 3oz lye, 1oz lemongrass scent with mica coloring.
Followed soap101 video in conjunction with directions from candles and supplies.
Followed soap101 video in conjunction with directions from candles and supplies.
I've always found HP ready to unmold as soon as it's completely cool.
^^^ me too
SunRiseArts
Well-Known Member
I made a lot of HP. I always wait 24 hours to be on the safe side
But I guess it depends on recipe and your preference. If your mold is silicone, touch the bottom with tiny pressure, and if it is hard, go ahead.
But I guess it depends on recipe and your preference. If your mold is silicone, touch the bottom with tiny pressure, and if it is hard, go ahead.
BroknArrw
Well-Known Member
I checked after 12 hours and it's hard but put back into mold to cut in the morning
Don't wait too long, HP soap gets pretty hard pretty fast. I tend to cut mine as soon as they get to room temp when I can, certainly don't wait past the next morning, and they are quite firm even then.
You can remove the soap from the mold as soon as it's firm enough not to sag, but it will stay liquid in the center for a while. Found that out by cutting too soon once or twice!
I've cut after about three hours with no issues, it hardens up pretty fast.
You can remove the soap from the mold as soon as it's firm enough not to sag, but it will stay liquid in the center for a while. Found that out by cutting too soon once or twice!
I've cut after about three hours with no issues, it hardens up pretty fast.
had that happen before too. The center wasn't quite liquid but was soft enough to run a tiny bit. Every bar had a little runny spot on it lol.